Effect of Sintering Temperature on Percentage of Tetragonal And Rhombohedral On Comparison of Zr / Ti (60/40)

Tamam Abimanyu, Rachmat Triandi, Masruroh Masruroh

Abstract


The synthesis of lead zirconate titanate (PZT) with ratio Zr:Ti of 60:40 have been conducted by sol gel method. The precursor of PZT were prepered from zirconium(IV) nitrate pentahydrate, titanium(IV) butoxide, lead(II) acetate trihydrate and 2-methoxyethanol and acetylaceton as a stabilizer solution. The PZT films deposited on Si substrate by spin coating method, then it was sintered at different temperature of 500°C, 600°C and 700°C. The crystal structure and composition of PZT films were observed by X-ray Diffraction (XRD) and Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX). The XRD results show the crystal orientation of PZT (100), (101), (110), (111), (002)T, (200)R, (200)T, (201) and (210), means that all PZT films are polycrystalline. Moreover, the orientation of (110) as temperature sintered of 600°C show the highes intensity than other temperature. The EDX results show mole fraction of Zr and Ti decrease compound with iniatial precursor. On the other hand, the mole fraction of O increase, which result in the existence of ZrO2 and TiO2 crystal.

 


Keywords


PZT; sol-gel technique; spin coating; sintering; zirconium nitrate

Full Text:

PDF

References


Wu, Yizhi (2011), Piezoelectric Response of Lead Titanate as A Function of Size, Master Tesis, Zernike Institute, University of Groningen.

Moret, Mona (1972), Preparation and Properties of Pb(Zr,Ti)O3 Films Grown by Metalorganic Chemical Vapor Deposition, Dutch Technology Foundation.

Bhaskar, Ankam, T.H. Chang, H.Y. Chang & S.Y. Cheng (2007), Low-Temperature Crystallization of Sol-Gel-Derived Lead Zirconate Titanate Thin Films Using 2.45 Ghz Microwaves, Journal Thin Solid Film, 515, 2891-2896.

Algafari, M. (2013), Studi Pengaruh Perbandingan Zr/Ti terhadap Struktur, Komposisi Fase dan Morfologi Kristal Lapisan Tipis PZT Pb(ZrxTi1-x)O3, Tesis, Universitas Brawijaya Malang.

Lapailaka, Titus (2013), Pengaruh Penambahan Pb dan Komposisi Zr/Ti terhadap Struktur, Komposisi Fase dan Morfologi Kristal Lapisan Tipis PZT dengan Metode Sol Gel Menggunakan Penstabil Asetil Aseton, Tesis, Universitas Brawijaya Malang.

Naat, Johnson (2014), Sintesis dan Karakterisasi Lapisan Tipis PZT Timbal Zirkonat Titanat dengan Variasi Penambahan Pelarut dan Kecepatan Putar Deposisi, Tesis, Universitas Brawijaya.

Zhang, Q. and Whatmore, R.W. (1998), Characterization of Particle Structure Pb(Zr0,3Ti0,7O3) Sols, Journal of the Korean Physical Society, 32, 572 -574.

Mu, Guohong, Shiyuan Y., Jufen Li & Mingyuan Gu (2007), Synthesis of PZT Nanocrystalline Powder by a Modified Sol-Gel Process Using Water as Primary Solvent Source, Journal of Materials Processing Technology, 182, 382-386.

Hikam, M., H. Darmasetiawan da T. Yogaraksa (2002), Studi Kekristalan (PbZrxTi1-xO3) Disiapkan dengan Pelapisan Putar (Spin Coating), Jurnal Sains Materi Indonesia: 4(1), 16-19.

Meng, X.J., Cheng, J.G., Li, B., Guo, S. L., Ye, H.J., and Chu, J.H (2000), Low-Temperature Preparation of Highly (111) Oriented PZT Thin Films by A Modified Sol Gel Technique, Journal of Crystal Growth: 208, 541-545.

Wang, G; Meng, X. J; Yun, J; Lai, Z; Guo, S; & Chu, J (2001), Effect of Hydrolysis On Properties of PbZr0.5T0.50O3 Ferroelectric Thin Films Derived from A Modified Sol–Gel Process, Journal of Crystal Growth: 233, 269-274.

Lee, Byeong Woo (2004), Synthesis and Characterization of Compositionally Modified PZT by Wet Chemical Preparation from Aqueous Solution, Journal of the European Ceramic Society, 24, 925-929.

Bhaskar, Ankam, T.H. Chang, H.Y. Chang & S.Y. Cheng (2007), Low-Temperature Crystallization of Sol-Gel-Derived Lead Zirconate Titanate Thin Films Using 2.45 Ghz Microwaves, Journal Thin Solid Film: 515, 2891-2896.

Bhatt, S. S., Chaudhry S. C, Sharma, N & Gupta, S (2010), Synthesis of Nano Crystalline Spatulae of Lead Zirconate Titanate (PbZr0.52Ti0.48O3), Natural Science, 2, 12-17.

Chang, Tien-I, Jow-Lay Huang, Hong-Ping Lin, Sheng-Chang Wang, Horng-Hwa Lu, Long Wu, Jen-Fu Lin (2006), Effect of Drying Temperature on Structure, Phase Transformation of Sol–Gel-Derived Lead Zirconate Titanate Powders, Journal of Alloys and Compounds: 414, 24-229.




DOI: http://dx.doi.org/10.21776/ub.natural-b.2015.003.02.3

Refbacks

  • There are currently no refbacks.